Calificación | C | Mn | Si | P | S | < p>Cr | Mo | Ni | N | otro | ||
321 | mín. máx. | - 0,08 | - 2,0 | - 0,75 | - 0,045 | - 0,030 | < p>17.0 19.0 | - | 9.0 12.0< /p> | - 0,10 | Ti=5(C+N) 0,70 | |
Grado | Resistencia a la tracción (MPa) min | Límite elástico 0,2% Resistencia (MPa) min | Alargamiento (% en 50 mm) mín | Dureza | ||
Rockwell B (HR B) máx | Brinell (HB) máx< /strong> | |||||
321 | 515 | 205 | 40 | 95 | 217 | |
Calificación | Densidad (kg/m3) | Módulo elástico (GPa) | < td colspan="3">< strong>Conductividad térmica (W/m.K) | Calor específico 0-100°C (J/kg.K)< /strong> | Resistividad eléctrica (nΩ.m) | ||||
0-100°C | 0-315°C | 0-538°C | a 100°C< /strong> | a 500°C | |||||
321 | 8027 | 193 | 16,6 | 17,2 | 18,6 | 16,1 | 22,2 | 500 | 720 |